S-glass fiber is silicon-aluminum-magnesium system glass fiber, which has high strength. This fiber is independently developed and put into production by our company to meet the needs of national defense and military industries.
Compared with alkali-free E glass fiber, tensile strength of S glass fiber is increased by 30-40%, the elastic modulus is increased by 16-20%, and the temperature resistance is increased by 100-150 °C.
The fatigue resistance of the reinforced material products with S glass fiber is increased by nearly 10 times, and the
S glass fiber offers the ultimate physical properties including high strength, compressive strength, large elongation at
break, toughness, and has the characteristics of aging resistance, corrosion resistance, and excellent resin penetration.
Widely used in various high-performance glass fiber reinforced materials such as projectile shells, phenolic grilles, CNG cylinders, reinforcement rings, fiber optic cable reinforcement yarns, sports equipment.
S-glass fiber is silicon-aluminum-magnesium system glass fiber, which has high strength. This fiber is independently developed and put into production by our company to meet the needs of national defense and military industries.
Compared with alkali-free E glass fiber, tensile strength of S glass fiber is increased by 30-40%, the elastic modulus is increased by 16-20%, and the temperature resistance is increased by 100-150 °C.
The fatigue resistance of the reinforced material products with S glass fiber is increased by nearly 10 times, and the
S glass fiber offers the ultimate physical properties including high strength, compressive strength, large elongation at
break, toughness, and has the characteristics of aging resistance, corrosion resistance, and excellent resin penetration.
Widely used in various high-performance glass fiber reinforced materials such as projectile shells, phenolic grilles, CNG cylinders, reinforcement rings, fiber optic cable reinforcement yarns, sports equipment.
● High tensile strength
● High elastic modulus
● High compressive strength, large elongation at break
● Good toughness, resistance of aging, corrosion
● Excellent resin penetration
● High tensile strength
● High elastic modulus
● High compressive strength, large elongation at break
● Good toughness, resistance of aging, corrosion
● Excellent resin penetration
Item | Unit | Test Method | Standard value | |
Code | EFG-S-735 | EFG-S-400 | ||
Linear density | Tex | ISO 1889:1997 | 735(±36.7) | 400(±20) |
yds/lb | 675 | 1222 | ||
Cv. | % | ISO 1889:1997 | <5 | <5 |
Loss on ignition | % | ISO1887:1995 | 0.8±0.3 | 0.8±0.3 |
Moisture Content | % | ISO3344:1997 | <0.2 | <0.2 |
Strand Tensile Strength | MPa | ASTM D 2343 | >2758 | >2758 |
Test condition | 1. Humility: 48% for EFG-S-400; 52% for EFG-S-735 2. . Room temperature: 22℃ |
Item | Unit | Test Method | Standard value | |
Code | EFG-S-735 | EFG-S-400 | ||
Linear density | Tex | ISO 1889:1997 | 735(±36.7) | 400(±20) |
yds/lb | 675 | 1222 | ||
Cv. | % | ISO 1889:1997 | <5 | <5 |
Loss on ignition | % | ISO1887:1995 | 0.8±0.3 | 0.8±0.3 |
Moisture Content | % | ISO3344:1997 | <0.2 | <0.2 |
Strand Tensile Strength | MPa | ASTM D 2343 | >2758 | >2758 |
Test condition | 1. Humility: 48% for EFG-S-400; 52% for EFG-S-735 2. . Room temperature: 22℃ |
6kgs/roll (13lbs/spool), 4rolls/carton, 18cartons/pallet
6kgs/roll (13lbs/spool), 4rolls/carton, 18cartons/pallet
This product should be stored in a dry, ventilated and rainproof place, with temperatures from 5℃to 35℃ and humidity between 35% and 65%. It is recommended to be kept in intact package when not used to avoid damp.
This product should be stored in a dry, ventilated and rainproof place, with temperatures from 5℃to 35℃ and humidity between 35% and 65%. It is recommended to be kept in intact package when not used to avoid damp.