Flame Retardant Non woven fabric with TPU Coated

Share to:

Flame Retardant Non woven fabric with TPU Coated

An ideal material for curtain, sunshade roofs

Thickness:	2mm
Availability:

Quantity:



Inquire Add to Basket

Brand:
NJEFG

Product Description
Application
Technical Data
Download

Flame Retardant Non woven fabric has non woven polyester mat as its base mat with flame retardant treatment, then coated with TPU agent on both sides. White film on one side and black film on the other.

The black side has feature of anti - ultraviolet, flame retardancy. And the white side is anti-age, anti-yellow change.

It is a ideal curtain,sunshade materials, usually used as curtains, sunshade roofs...

CHARACTERISTICS

1. flame retardant

2. anti - ultraviolet

3. anti-age

4. anti-yellow change

TPU coated TPU coated canvas TPU coated cotton TPU coated polyester TPU coated fabric TPU coated webbing

ITEM	TEST RESULT	TEST STANDARD	REMARK
Assessment of the potential to phenolic yellowing of material	White film of back Unit: grade Color staining: grade 4	ISO 105 X18:2007
Tearing Strength ISO 13937.2:2000 Single-shaped method	Warp: 110N Weft: 160(CT)	ISO 13937.2:2000 Single-shaped method	CT=Cross Wise Tear
Water Resistance: Rain Test	UPF:>50 UPF(AV):>500 T(UVA): 0.02% T(UVB): 0.02%	EN 13758.1:2001/A1:2006

Edge ignition	Warp direction			Weft direction
Edge ignition	1	2	3	1	2	3
Duration of flaming (s)	8.69	13.64	38.02	13.93	18.58	15.07
Duration of afterglow (s)	0.0	0.0	0.0	0.0	0.0	0.0
Damaged length (mm)	147	133	150	129	145	177
The time in seconds from the start of the application of the test flame until the severance of the lower (first) marker thread	N/A	N/A	N/A	N/A	N/A	N/A
The time in seconds from the start of the application of the test flame until the severance of the middle (second) marker thread	N/A	N/A	N/A	N/A	N/A	N/A
The time in seconds from the start of the application of the test flame until the severance of the upper (third) marker thread	N/A	N/A	N/A	N/A	N/A	N/A
TEST STANDSARD: ISO 6941:2003 Procedures B, edge ignition Test condition: Temperature 20.4℃， Relative humidity 65.7% Ignition time: 10 seconds Remark: N/A=flame has been extinguished before reaching to the tag line

ITEM	TEST RESULT	TEST STANDARD	REMARK
Assessment of the potential to phenolic yellowing of material	White film of back Unit: grade Color staining: grade 4	ISO 105 X18:2007
Tearing Strength ISO 13937.2:2000 Single-shaped method	Warp: 110N Weft: 160(CT)	ISO 13937.2:2000 Single-shaped method	CT=Cross Wise Tear
Water Resistance: Rain Test	UPF:>50 UPF(AV):>500 T(UVA): 0.02% T(UVB): 0.02%	EN 13758.1:2001/A1:2006

Edge ignition	Warp direction			Weft direction
Edge ignition	1	2	3	1	2	3
Duration of flaming (s)	8.69	13.64	38.02	13.93	18.58	15.07
Duration of afterglow (s)	0.0	0.0	0.0	0.0	0.0	0.0
Damaged length (mm)	147	133	150	129	145	177
The time in seconds from the start of the application of the test flame until the severance of the lower (first) marker thread	N/A	N/A	N/A	N/A	N/A	N/A
The time in seconds from the start of the application of the test flame until the severance of the middle (second) marker thread	N/A	N/A	N/A	N/A	N/A	N/A
The time in seconds from the start of the application of the test flame until the severance of the upper (third) marker thread	N/A	N/A	N/A	N/A	N/A	N/A
TEST STANDSARD: ISO 6941:2003 Procedures B, edge ignition Test condition: Temperature 20.4℃， Relative humidity 65.7% Ignition time: 10 seconds Remark: N/A=flame has been extinguished before reaching to the tag line