PVC floor is widely used because of light weight, beautiful design, not easy to wear and tear and easy to operation. However, due to the addition of many filling materials, PVC floor has lower strength and greater brittleness. PVC material has the characteristic that it is easy to cause thermal expansion and contraction, so PVC flooring in public place such as airport, mall, hotel, hospital, etc., are easy to bubble and hard to get repaired. According to this phenomenon, NJEFG developed PVC impregnated fiberglass mat for PVC flooring, PVC impregnated fiberglass mat is used as stabilizing layer of PVC floor.
The fiberglass mat can be 30g/m2, 40g/m2 and 50g/m2 or according to the customer’s demand. And the minimum final weight of the PVC impregnated fiberglass mat can be around 120g/m2, the popular weight is 150g/m2 and 250g/m2, the final weight can be done according to the customer’s requirement.
PVC floor is widely used because of light weight, beautiful design, not easy to wear and tear and easy to operation. However, due to the addition of many filling materials, PVC floor has lower strength and greater brittleness. PVC material has the characteristic that it is easy to cause thermal expansion and contraction, so PVC flooring in public place such as airport, mall, hotel, hospital, etc., are easy to bubble and hard to get repaired. According to this phenomenon, NJEFG developed PVC impregnated fiberglass mat for PVC flooring, PVC impregnated fiberglass mat is used as stabilizing layer of PVC floor.
The fiberglass mat can be 30g/m2, 40g/m2 and 50g/m2 or according to the customer’s demand. And the minimum final weight of the PVC impregnated fiberglass mat can be around 120g/m2, the popular weight is 150g/m2 and 250g/m2, the final weight can be done according to the customer’s requirement.
Lower unit weight, high strength, uniform surface
Significantly reduces the expansion rate of the floor
Makes floor more suitable for heating
Increase the producing efficiency of floor and rate of finished product
Free of formaldehyde, environment friendly
Lower unit weight, high strength, uniform surface
Significantly reduces the expansion rate of the floor
Makes floor more suitable for heating
Increase the producing efficiency of floor and rate of finished product
Free of formaldehyde, environment friendly
Code | fiberglass floor mat | Total unit weight | Tensile strength MD | Tensile strength CD | Thickness | Moisture | Paper core diameter |
g/m2 | g/m2 | N/5CM | N/5CM | mm | % | mm | |
F-PC-150 | 30 | 150(±20) | ≥150 | ≥100 | 0.3(±0.05) | ≤1 | 76 |
F-PC-250 | 40 | 250(±30) | ≥170 | ≥110 | 0.35(±0.05) | ≤1 | 76 |
Standard | GB/T 24218.1-2009 | GB3820-1997 | GB/T 24218.3-2009 | GB/T11966-1989 | |||
Remark: 1. Roll width 1m, 1.11m (±2mm); roll length: 1300m;
2. Roll diameter: 70cm (±2 0mm)
Code | fiberglass floor mat | Total unit weight | Tensile strength MD | Tensile strength CD | Thickness | Moisture | Paper core diameter |
g/m2 | g/m2 | N/5CM | N/5CM | mm | % | mm | |
F-PC-150 | 30 | 150(±20) | ≥150 | ≥100 | 0.3(±0.05) | ≤1 | 76 |
F-PC-250 | 40 | 250(±30) | ≥170 | ≥110 | 0.35(±0.05) | ≤1 | 76 |
Standard | GB/T 24218.1-2009 | GB3820-1997 | GB/T 24218.3-2009 | GB/T11966-1989 | |||
Remark: 1. Roll width 1m, 1.11m (±2mm); roll length: 1300m;
2. Roll diameter: 70cm (±2 0mm)
This product should be stored in a dry, ventilated and rainproof place, with temperatures from 5℃to 35℃ and humidity between 35% and 65%. It is recommended to be kept in intact package when not used to avoid damp.
This product should be stored in a dry, ventilated and rainproof place, with temperatures from 5℃to 35℃ and humidity between 35% and 65%. It is recommended to be kept in intact package when not used to avoid damp.