Fiberglass Battery Separator Mat is a material with the property of good fiber dispersion, uniform thickness, potassium permanganate reducing content, low content of Cl-, Fe3+ and other trace elements and acid penetrating fast. The battery made of fiberglass tissue has high starting current, excellent anti - vibration performance , slow battery power attenuation and long service life.
【Characteristics】
Smooth Surface, Uniform Thickness
Good Acid Liquor Absorption Ability
Good Acid Resistance，Moderate Stiffness
Low Potassium Permanganate Content,
Low Trace Element Content
Fiberglass Battery Separator Mat is a material with the property of good fiber dispersion, uniform thickness, potassium permanganate reducing content, low content of Cl-, Fe3+ and other trace elements and acid penetrating fast. The battery made of fiberglass tissue has high starting current, excellent anti - vibration performance , slow battery power attenuation and long service life.
【Characteristics】
Smooth Surface, Uniform Thickness
Good Acid Liquor Absorption Ability
Good Acid Resistance，Moderate Stiffness
Low Potassium Permanganate Content,
Low Trace Element Content
Widely used as a lead -acid battery separator substrate.
Widely used as a lead -acid battery separator substrate.
Product code
Thickness
（mm）
Chlorine content
（%）
Iron content
（%）
Potassium permanganate restore content（ml/g）
F-GB-0.3
0.3±0.03
≤0.003
≤0.005
≤15
F-GB-0.4
0.4±0.03
≤0.003
≤0.005
≤15
F-GB-0.5
0.5±0.04
≤0.003
≤0.005
≤15
F-GB-0.6
0.6±0.04
≤0.003
≤0.005
≤15
F-GB-0.8
0.8±0.05
≤0.003
≤0.005
≤15
Remark: Other specification can be tailored as per customers’ demand on size and property.
Product code
Thickness
（mm）
Chlorine content
（%）
Iron content
（%）
Potassium permanganate restore content（ml/g）
F-GB-0.3
0.3±0.03
≤0.003
≤0.005
≤15
F-GB-0.4
0.4±0.03
≤0.003
≤0.005
≤15
F-GB-0.5
0.5±0.04
≤0.003
≤0.005
≤15
F-GB-0.6
0.6±0.04
≤0.003
≤0.005
≤15
F-GB-0.8
0.8±0.05
≤0.003
≤0.005
≤15
Remark: Other specification can be tailored as per customers’ demand on size and property.